Hot Rolled 1.1210 S50c C50 Ck50 1050 Carbon Steel Sheet

Model NO.: 1.1210/ S50c/ C50/ Ck50/ 1050
Special Use: High-strength Steel Plate, Wear Resistant Steel
Stock: Stock
Name: Hot Rolled 1.1210 S50c C50 Ck50 1050 Carbon Steel
Shape: Round Bars/Flat Bar/Plate/Coil
Sample: Free
Heat Treatment: Annealed
Surface: Black/Peeling/Polishing/Machined
Delivery Condition: Hot Rolled or Forged/ Peeled or Black Surface
Test: SGS/Ut100%/Elements Testing
Certificate: ISO/Mill Certificate
Service: 24 Hours Online
Experience: More Than Ten Years Manufacturer Experience
Trademark: Songshun
Transport Package: Standard Seaworthy Packing
Specification: Diameter 16-600mm
Origin: China
HS Code: 7228309000
Hot Rolled 1.1210 S50c C50 Ck50 1050 Carbon Steel Sheet 


Size of 1050 carbon steel

Diameter(mm):20~600   Length (mm):1000~6000
Plate
Thickness(mm):Max:800    Width (mm):Max:2200   Length (mm):Max:6000
The specification can be customized.

Chemical Compositions
C Si Mn P S Cr Ni
0.47-0.55 0.17-0.37 0.5-0.8 Max0.035 Max0.035 Max0.25 Max0.3


Similar Grade
GB AISI DIN JIS
50 1050 1.1210 S50C
 

Hardness

Annealed ≤241HB, Cold drawn ≤285HB.

 

Surface Treatment

Plate: Origin Black, Orign cold rolled bright, Machined, Grinded

Bar:   Origin Black, Orign cold rolled(drawn) bright, Turned, Peeled, Grinded

 

Heat Treatment

1) Forging

Preheat the steel carefully, then raise temperature to 1100°C for forging. Do not forge below 850°C. After forging cool slowly, preferably in a furnace.

 

2)Annealing

Heat slowly to 680-710°C, soak well. Cool slowly in the furnace.

 

3)Hardening

Heat the component slowly to 820-860°C and allow it to be heated through. Quench in oil or water.

 

4)Tempering

Temper immediately after quenching whilst tools are still hand warm. Re-heat the C50 to the tempering temperature then soak for one hour per 25 millimetre of total thickness (2 hours minimum) Cool in air. For most applications temper between 550-660°C.

 

5)Welding

We recommend you contact your welding consumables supplier who should provide you full assistance and information on welding C50 steel.

 

6)Heat Treatment 

Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each C50 steel component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities. Please consult your heat treatment provider for full guidance on heat treatment of C50 carbon steel.

 

Features

1. Charateristics

C50 is widely used for components that require better properties than mild steel but does not justify the costs of an alloy steel. Available from stock in bar, C50 can be cut to your requirements. We also offer flame cut plates cut to your required sizes and normalised. C50 flame cut plates can be supplied surface ground or precision ground.

 

2. Applications

 

C50 is widely used for many general engineering applications. Typical applications include tools, shafts, nuts, bolts, connecting rods, screws, rollers.



Alloy Steel 4140 1.7225 Scm440 42CrMo4 Cold Drawn Round Bars
Alloy Steel 4140 1.7225 Scm440 42CrMo4 Cold Drawn Round Bars
 

All Poplar Laminated Veneer Lumber For Package, LVL Packing Box, Laminated Veneer Lumber Pallet

Features:

high strength, high toughness, good stability, precise specifications,
ratio of solid lumber in strength, toughness increased by 3 times. This product
is mainly used in various types of packaging plant, wood products factory,
especially machinery, glass, chemical and other products of the export
packaging, in addition to the construction of a wide range of formwork
components, building beams, car panels, furniture, floor, room decoration wood
keel, etc..

LVL-Plywood-1220X2440mm-or-as-your-request-

All Poplar Laminated Veneer Lumber For Package

All Poplar Laminated Veneer Lumber For Package, LVL Packing Box, Laminated Veneer Lumber Pallet

HUAIAN HONGXIN INTERNATIONAL TRADE CO.,LTD , http://www.hongxin-trade.com